Zirconia (YSZ) Molamu o silang mecha ea litaba
Ha ho bapisoa le melamu ea alumina Yttria stabilized zirconia (YSZ YTZP) e ne e ka mamella mocheso o phahameng le ho feta.Zirconia e boetse e na le kutu e ntle le ho apara ho hanyetsa.E le thepa e hanyetsang haholo, mocheso o sebetsang oa lithupa tsa zirconia o ka ba holimo ho 1900C 'me oa tsitsa ho lik'hemik'hale tse ngata tse senyang hape.Li-crucible tsa Zirconia li boetse li fana ka ts'ebetso e tlase haholo ea mocheso le motlakase, ho etsa hore e be se loketseng bakeng sa lits'ebetso, e hloka insulating ea motlakase le ea mocheso.
Leha ho le joalo, ho fapana le boron nitride, molamu oa Zirconia ha o khothalletsoe hore o sebelisoe e le thepa e tala bakeng sa mosebetsi o eketsehileng oa machining, ka lebaka la boima bo phahameng le ho apara ho hanyetsa.
Lithupa tsa Yiho YSZ
Joalo ka morekisi ea ka sehloohong oa thepa ea ceramic e etselitsoeng esale pele lebopong le ka bochabela la USA, QS Advanced Materials e sebetsa haufi-ufi le baetsi ba lisebelisoa tsa ceramic sintering le machining ho fana ka lihlahisoa tsa zirconia tse tsitsitseng ka theko e ntle haholo.Re tsoela pele ho fana ka li-crucibles tsa zirconia le lisebelisoa tse ling tsa motheo.Ka li-stocks tse felileng, le bokhoni bo phahameng ba tlhahiso, melemo ea nako le litšenyehelo e fanoa.
Likopo tsa likarolo tsa Yttria Stabilized Zirconia (YSZ,YTZP).
• E sebelisoa bakeng sa ho sila lisebelisoa tsa letsopa, lisebelisoa tsa makenete le lisampole tsa tlhaho
• Likarolo tse ling tsa mochini oa ho beleha le tse ling
• Likarolo tse khethehileng tsa pompo
Ts'ebetso ea zirconia ceramics
Boima: 6.05 g/cm3
Ho monya ha metsi: <0.05%
Mocheso oa ho thunya: 1550 °C
Matla: 1350 HV
Matla a khatello: 25000 MPa
Coefficient ea ho eketsa mocheso: 9.5x10-6 /°C
Matla a ho kobeha: 950 MPa
Sephutheloana
Joalo ka thepa ea ceramic, thepa ea Zirconia e ntse e fokola, leha YSZ e fetoha habonolo.Lithupa tsa rona tsa zirconia hangata li ts'oaroa ka mekotleng ea polasetiki ka vacuum, 'me li sireletsa ka foam e boima.
Leqephe la Thepa
| Thepa | Diyuniti | 95 Alumina | 99 Alumina | Zirconia |
| Botenya | cm3 | 3.65 | 3.92 | 5.95 - 6.0 |
| Ho Monyeha ha Metsi | ％ | 0 | 0 | 0 |
| Coefficient ea Katoloso ea Thermal | 10-6 / K | 7.9 | 8.5 | 10.5 |
| HV boima | Mpa | 1400 | 1650 | 1300 - 1365 |
| Flexural Strength @ Mocheso oa Kamore | Mpa | 280 | 310 | 950 |
| Flexural Strength @ 700℃ | Mpa | 220 | 230 | 210 |
| Matla a Khatellang @ Mocheso oa Kamore | Mpa | 2000 | 2200 | 2000 |
| Ho thatafala ha Fracture | Mpa * m½ | 3.8 | 4.2 | 10 |
| Mocheso Conductivity @ Mocheso oa Kamore | W / m * k | 18-25 | 26-30 | 2.0 - 2.2 |
| Motlakase Resistivity @ Mocheso oa Kamore | Ω*mm2 / m | ~1015 | ~1016 | ~1015 |
| Mocheso o Phahameng oa Kopo | ℃ | 1500 | 1750 | 1050 |
| Ho hanyetsa Acid Alkaline | / | Phahameng | Phahameng | Phahameng |
| Dielectric Constant | / | 9.5 | 9.8 | 26 |
| Thermal Shock Resistance | Δ T ( ℃ ) | 220 | 180-200 | 282 - 350 |
| Matla a Tensile @ 25℃ | Mpa | 200 | 248 | 252 |